Thursday, July 20, 2006

High-Strength Low-Alloy Steels

High-strength low-alloy (HSLA) steels, or microalloyed steels, are designed to provide better mechanical properties and/or greater resistance to atmospheric corrosion than conventional carbon steels in the normal sense because they are designed to meet specific mechanical properties rather than a chemical composition.

The HSLA steels have low carbon contents (0.05-0.25% C) in order to produce adequate formability and weldability, and they have manganese contents up to 2.0%. Small quantities of chromium, nickel, molybdenum, copper, nitrogen, vanadium, niobium, titanium and zirconium are used in various combinations.

HSLA Classification:

* Weathering steels, designated to exhibit superior atmospheric corrosion resistance
* Control-rolled steels, hot rolled according to a predetermined rolling schedule, designed to develop a highly deformed austenite structure that will transform to a very fine equiaxed ferrite structure on cooling
* Pearlite-reduced steels, strengthened by very fine-grain ferrite and precipitation hardening but with low carbon content and therefore little or no pearlite in the microstructure
* Microalloyed steels, with very small additions of such elements as niobium, vanadium, and/or titanium for refinement of grain size and/or precipitation hardening
* Acicular ferrite steel, very low carbon steels with sufficient hardenability to transform on cooling to a very fine high-strength acicular ferrite structure rather than the usual polygonal ferrite structure
* Dual-phase steels, processed to a micro-structure of ferrite containing small uniformly distributed regions of high-carbon martensite, resulting in a product with low yield strength and a high rate of work hardening, thus providing a high-strength steel of superior formability.

The various types of HSLA steels may also have small additions of calcium, rare earth elements, or zirconium for sulfide inclusion shape control.
Low-alloy Steels
Low-alloy steels constitute a category of ferrous materials that exhibit mechanical properties superior to plain carbon steels as the result of additions of alloying elements such as nickel, chromium, and molybdenum. Total alloy content can range from 2.07% up to levels just below that of stainless steels, which contain a minimum of 10% Cr.

For many low-alloy steels, the primary function of the alloying elements is to increase hardenability in order to optimize mechanical properties and toughness after heat treatment. In some cases, however, alloy additions are used to reduce environmental degradation under certain specified service conditions.

As with steels in general, low-alloy steels can be classified according to:

* Chemical composition, such as nickel steels, nickel-chromium steels, molybdenum steels, chromium-molybdenum steels
* Heat treatment, such as quenched and tempered, normalized and tempered, annealed.

Because of the wide variety of chemical compositions possible and the fact that some steels are used in more than one heat-treated, condition, some overlap exists among the alloy steel classifications. In this article, four major groups of alloy steels are addressed: (1) low-carbon quenched and tempered (QT) steels, (2) medium-carbon ultrahigh-strength steels, (3) bearing steels, and (4) heat-resistant chromium-molybdenum steels.

Low-carbon quenched and tempered steels combine high yield strength (from 350 to 1035 MPa) and high tensile strength with good notch toughness, ductility, corrosion resistance, or weldability. The various steels have different combinations of these characteristics based on their intended applications. However, a few steels, such as HY-80 and HY-100, are covered by military specifications. The steels listed are used primarily as plate. Some of these steels, as well as other, similar steels, are produced as forgings or castings.

Medium-carbon ultrahigh-strength steels are structural steels with yield strengths that can exceed 1380 MPa. Many of these steels are covered by SAE/AISI designations or are proprietary compositions. Product forms include billet, bar, rod, forgings, sheet, tubing, and welding wire.

Bearing steels used for ball and roller bearing applications are comprised of low carbon (0.10 to 0.20% C) case-hardened steels and high carbon (-1.0% C) through-hardened steels. Many of these steels are covered by SAE/AISI designations.

Chromium-molybdenum heat-resistant steels contain 0.5 to 9% Cr and 0.5 to 1.0% Mo. The carbon content is usually below 0.2%. The chromium provides improved oxidation and corrosion resistance, and the molybdenum increases strength at elevated temperatures. They are generally supplied in the normalized and tempered, quenched and tempered or annealed condition. Chromium-molybdenum steels are widely used in the oil and gas industries and in fossil fuel and nuclear power plants.