Flake graphite iron finds use due to: its cheapness and ease of machining; low-melting temperature (1140-1200°C); ability to take good casting impressions; wear resistance; high damping capacity; a reasonable tensile strength of 108-340 MPa associated with a very high compressive strength, making it very suitable for applications requiring rigidity and resistance to wear. The different types vary from grey iron which is machinable to either mottled or white iron which is not easily machinable. The white irons of suitable composition can be annealed to give malleable cast iron. During the last thirty years much development work has taken place and it has been found worth while to add even expensive elements to the cheap metal because vastly improved properties result. The new irons formed by alloying or by special melting and casting methods are becoming competitors to steel. The various irons can be classified as shown in Fig. 1 based on the form of graphite and the type of matrix structure in which it is embedded. The metallurgical structure, composition and section of the casting largely govern the engineering properties. One of the differences between cast iron and steel is the presence of a large quantity of carbon, generally 2-4%, and frequently high silicon contents. While carbon in ordinary steel exists as cementite (Fe3C), in cast iron it occurs in two forms: stable form-graphite; unstable form-cementite, analysed as combined carbon. CAST IRON Grey machinable iron White, unmachinable iron no graphite Flake Graphite Spheroidal Graphite Pearlitic Martensitic Ferritic Pearlitic Austenitic Martensitic Malleable iron temper carbon graphite Ferritic Pearlitic Blackheart Thin Whiteheart Whiteheart Special Malleable Figure 1. Classification of cast iron (Pearce) Graphite is grey, soft, and occupies a large bulk, hence counteracting shrinkage; while cementite is intensely hard, with a density of the same order as iron. On the relative amounts, shape and the distribution of these two forms of carbon largely depend the general properties of the iron. The factors mainly influencing the character of the carbon are: The rate of cooling. The chemical composition. The presence of nuclei of graphite and other substances. 1. Rate of cooling. A high rate of cooling tends to prevent the formation of graphite, hence maintains the iron in a hard, unmachinable condition. If the casting consists of varying sections then the thin ones will cool at a much greater rate than the thick. Consequently, the slowly cooled sections will be grey and the rapidly cooled material will be chilled. These points are illustrated in Fig. 2, which shows the variation in hardness of a step casting. Figure 2. The relation between the rate of cooling and hardness as indicated by sections of varying thickness 2. The effect of chemical composition. Carbon lowers the melting-point of the metal and produces more graphite. Hence it favours, a soft, weak iron. Silicon slightly strengthens the ferrite but raises the brittle transition temperature, Indirectly, however, it acts as a softener by increasing the tendency of the cementite to slip up into graphite and ferrite. Fig. 3 shows the relation between the carbon and silicon contents in producing the different irons for one rate of cooling. It will be noted that either a high carbon and low silicon or low carbon and high silicon content give grey iron; the fracture can, therefore, be misleading as to analysis, especially if the rate of cooling is not considered. The amounts of silicon, giving the maximum values for various properties, are also shown in Fig. 3. The percentage of silicon is varied according to the thickness of the casting. Sulphur and manganese. Sulphur can exist in iron, as either iron sulphide, FeS, or manganese sulphide, MnS. Sulphur as FeS tends to promote cementite producing a harder iron. When manganese is added, MnS is formed which rapidly coalesces and rises to the top of the melt. The first effect of the manganese is, therefore, to cause the formation of graphite due to its effect on the sulphur. The direct effect of manganese is to harden the iron, and this it will do when it exists in amounts greater than that required to combine with the sulphur-1 part sulphur to 1,72 part manganese. Phosphorus has a little effect on the graphite-cementite ratio; but renders the metal very fluid indirectly through the production of a low-melting constituent, which is readily recognised in the micro-structure (Fig. 4). In the production of sound castings of heavy section, phosphorus should be reduced to about 0,3% in order to avoid shrinkage porosity. Trace elements not normally considered in routine analyses can exert a profound influence upon the characteristics of cast iron. Examples are 0,1% of aluminium graphitises, antimony embrittles, lead, tellurium promotes carbide but reduces strength of iron; 0,003% of hydrogen can greatly affect soundness of castings and tends to coarsen graphite. Nitrogen behaves as a carbide stabiliser; oxygen has no specific effect. Figure 3. Diagram indicating the structures of iron resulting from variation of silicon and carbon contents Figure 4. Common grey iron showing ferrite (F), pearlite (P) and phosphide eutectic (PH) (x250). Ferrite is associated with the graphite. Note banded structure in the phosphide eutectic The carbon equivalent value. From Fig. 5 it will be seen that the eutectic E is at 4,3% carbon and irons with a greater carbon content will (under suitable conditions) start freezing by throwing out kish graphite of large size. With carbon contents progressively less than 4,3% normal graphite is formed in diminishing quantities until a mottled or white iron range is reached. Naturally other elements, especially silicon and phosphorus, affect the composition of the eutectic point in a complex alloy and a carbon equivalent value is suggested as an index which converts the amount of these elements into carbon replacement values. Figure 5. Iron-cementite equilibrium diagram Carbon equivalent value (CE) = Total C% + 1/3 (Si% + P%) For a given cooling rate the carbon equivalent value, therefore, determines how close a given composition of iron is to the eutectic (CE 4,3) and therefore how much free graphite is likely to be present, and consequently the probable strength in a given section: the carbon equivalent value is also a useful guide to chilling tendency of a given section, although it must be borne in mind that pouring temperature, cooling rate and alloying elements have a marked influence.

You want to be always up-to-date? Apply to Key to Steel eNews and receive fresh, leading-edge technical information and knowledge from the World's Most Comprehensive Steel Database. Search Knowledge Base Enter a phrase to search for: Search by Full text Keywords Headings Abstracts Subscribe to Key to Steel Now The Worlds Most Comprehensive Steel Properties Database Find out why the worldwide leaders like Alcatel, Alstom, Apple, Benteler, Bentley, Black&Decker, ChevronTexaco, ConocoPhillips, DaimlerChrysler, Dana, Delphi, Eaton, Ford, General Electric, General Dynamics, Halliburton, Hitachi, Honda, Hyundai, Livermore National Laboratory, Lloyds, Maxtor, Pirelli, Sandvik, Shell, Siemens, SSAB, Stanford University, Sulzer, Thyssen-Krupp, Total, Toyota, TÜV and many others joined the Database in the last 12 months only. And check out why are the high quality of services and focus to your needs multiply certified according to ISO 9001:2000 standards, the first in this industry. Subscribe to full-featured Key to Steel Database Now Register to the free part of the Database Download Key to Steel Fact Sheet Download Key to Steel Price List Key to Steel :: Trusted in 160 Countries Key to Steel: Focus on Quality Key to Steel offers you real, rock-solid and time-saving value. Fingertip access to full-featured Key to Steel Database covers ferrous alloys properties from 34 countries/standards and includes: More than 600,000 records More than 42,000 alloys Chemical composition Standard reference Application guidelines Mechanical properties Heat treatment details Properties on elevated temperatures Fatigue properties Most comprehensive tables of equivalent materials worldwide. High quality of Key to Metals Group activities is certified by German certification body TÜV CERT and by leading UK quality association UKAS. 138 View Quick Richmedia Tour Register to the free part of the Database Download Key to Steel Fact Sheet Download Key to Steel Price List Subscribe to full-featured Key to Steel Database Key to Steel :: Trusted in 160 Countries Be always up-to-date, FREE Because Key to Steel updates are FREE for our Subscribers. Moreover, when you subscribe, you get: Unlimited number and frequency of accesses and searches from Key to Steel Database Complete Knowledge Base of articles FREE Web Database updates every month and Key to Steel Database software updates as soon as they are implemented (for Web Edition). Three (3) FREE Key to Steel Database updates (for CD Edition). FREE Technical support and our special e-mail consulting services for additional information about steel materials. Subscribe to full-featured Key to Steel Database Now Register to the free part of the Database Key to Steel :: Trusted in 160 Countries Discover NEW Key to Steel Corporate Solutions With the new Corporate Solutions, you are getting the complete power of information and knowledge from the Key to Steel Database, always up-to-date, like it is your own, private resource, incorporated into your intranet. Find out more about these turn-key, maintenance-free solutions for you, visit Corporate Solutions.